Materials & grades
4340 / EN24 / 34CrNiMo6 / SNCM439 nickel-chromium-molybdenum steel
AISI 4340 is a medium-carbon nickel-chromium-molybdenum alloy steel, used hardened and tempered where high strength and toughness are needed in large sections. Its usual counterparts are 817M40 (formerly EN24) in the UK, 34CrNiMo6 (1.6582) in Europe, 40Ni6Cr4Mo3 in India and SNCM439 in Japan.
Names by standard
What it is called in each region
| Region | System | Designation | 規格 | Match |
|---|---|---|---|---|
| USA | AISI/SAE | 4340 | SAE J404; ASTM A29 (bar) | Same material |
| UNS | G43400 | — | Same material | |
| UK | BS 970-3 (1991) | 817M40Less nickel and more chromium than 4340. BS 970 alloy grades are superseded by EN 10083-3 but are still ordered by name, often as 817M40T. | BS 970-3 | Closest equivalent |
| BS 970 (1955 EN series) | EN24Superseded 1955 name for 817M40. Still the most-searched UK name; usually supplied hardened and tempered as EN24T. | — | Closest equivalent | |
| EU | EN 10027-1 name | 34CrNiMo6The EN grade most charts give for EN24 and 4340, but with lower carbon. Same name was used in the superseded DIN 17200. | EN 10083-3; EN ISO 683-2 | Closest equivalent |
| EN 10027-2 number | 1.6582 | EN 10083-3 | Closest equivalent | |
| EN 10027-1 name | 36CrNiMo4 (1.6511)Given by some charts. Its name indicates about 1% nickel, so it is a weaker match than 34CrNiMo6. | EN 10083-3 | Closest equivalent | |
| インド | IS 1570 | 40Ni6Cr4Mo3 | IS 1570 (Part 4):1988 | Closest equivalent |
| IS (pre-1974 designation) | 40Ni2Cr1Mo28Older Indian letter-symbol name still quoted for EN24. Superseded by the IS 1762 designation system used in IS 1570 (Part 4):1988. | IS 4368:1967 | Closest equivalent | |
| Japan | JIS G 4053 | SNCM439 | JIS G 4053 | Equivalent |
| JIS G 4053 | SNCM447Listed for 4340 in some references; the name indicates a higher-carbon grade of the same family. | JIS G 4053 | Closest equivalent |
On equivalence
- 4340 and EN24 (817M40) are routinely interchanged, but their chemistries differ: 817M40 has less nickel (1.30–1.70% against 1.65–2.00%) and more chromium (1.00–1.40% against 0.70–0.90%). The match is therefore marked closest.
- 34CrNiMo6 (1.6582) is the EN grade most charts give for both EN24 and 4340, but its carbon range is lower (0.30–0.38%). Saarstahl cross-references 34CrNiMo6 to 817M40 and 816M40 and to SAE 4337 and 4340.
- Some charts list 36CrNiMo4 (1.6511) for 4340. It contains about 1% nickel and is a weaker match.
- India: 40Ni6Cr4Mo3 in IS 1570 (Part 4):1988 is the closest listed grade to EN24. Charts also give 40Ni2Cr1Mo28 (pre-1974 name) or 40NiCr4Mo3; 40Ni6Cr4Mo2 is a lower-molybdenum grade (0.10–0.20% Mo). IS 1570 (Part 4) leaves phosphorus and sulphur limits to the product specification.
- Japan: SNCM439 overlaps 4340 closely. Its limits here come from a supplier listing of JIS G 4053, not the JIS text, and should be checked against the standard. Some references list SNCM447 instead, which is a higher-carbon grade.
- Compare grades at the same condition and ruling section. The EN 10083-3 minimum yield of 34CrNiMo6 falls from 1000 MPa (diameter ≤16 mm) to 600 MPa (160–250 mm).
Chemical composition
Composition limits, mass %
| Element | 4340USA · AISI/SAE 4340 (bar) | 817M40 (EN24)UK · BS 970-3 | 34CrNiMo6 (1.6582)EU · EN 10083-3 | 40Ni6Cr4Mo3インド · IS 1570 (Part 4):1988 | SNCM439Japan · JIS G 4053 |
|---|---|---|---|---|---|
| C | 0.38–0.43 | 0.36–0.44 | 0.30–0.38 | 0.35–0.45 | 0.36–0.43 |
| Si | 0.15–0.35 | 0.10–0.35 | ≤0.40 | 0.10–0.35 | 0.15–0.35 |
| Mn | 0.60–0.80 | 0.45–0.70 | 0.50–0.80 | 0.40–0.70 | 0.60–0.90 |
| P | ≤0.035 | ≤0.035 | ≤0.025 | — | ≤0.030 |
| S | ≤0.040 | ≤0.040 | ≤0.035 | — | ≤0.030 |
| Cr | 0.70–0.90 | 1.00–1.40 | 1.30–1.70 | 0.90–1.30 | 0.60–1.00 |
| Ni | 1.65–2.00 | 1.30–1.70 | 1.30–1.70 | 1.25–1.75 | 1.60–2.00 |
| Mo | 0.20–0.30 | 0.20–0.35 | 0.15–0.30 | 0.20–0.35 | 0.15–0.30 |
Mechanical properties
Strength and hardness
| Condition | Tensile strength | Yield strength | Elongation | Hardness |
|---|---|---|---|---|
| AnnealedTypical values, not specified minimumsAZoM, AISI 4340 alloy steel (UNS G43400) | 745 MPa108 ksi | 470 MPa68.2 ksi | 22 % | 217 HB |
| Hardened and tempered, condition TBS 970 condition T; values depend on ruling sectionSmiths Metal Centres, EN24 technical datasheet | 850–1000 MPa123–145 ksi | ≥650 MPa≥94 ksi | ≥13 % | 248–302 HB |
| Hardened and tempered, condition VBS 970 condition V; values depend on ruling sectionSmiths Metal Centres, EN24 technical datasheet | 1000–1150 MPa145–167 ksi | ≥850 MPa≥123 ksi | ≥12 % | 293–352 HB |
| Quenched and tempered (+QT)Specified, diameter 16–40 mm (thickness 8–20 mm); yield and elongation are minimumsEN 10083-3, 34CrNiMo6, via Saarstahl datasheet | 1100–1300 MPa160–189 ksi | ≥900 MPa≥131 ksi | ≥10 % | — |
| Quenched and tempered (+QT)Specified, diameter 40–100 mm (thickness 20–60 mm); yield and elongation are minimumsEN 10083-3, 34CrNiMo6, via Saarstahl datasheet | 1000–1200 MPa145–174 ksi | ≥800 MPa≥116 ksi | ≥11 % | — |
| Quenched and tempered (+QT)Specified, diameter 100–160 mm (thickness 60–100 mm); yield and elongation are minimumsEN 10083-3, 34CrNiMo6, via Saarstahl datasheet | 900–1100 MPa131–160 ksi | ≥700 MPa≥102 ksi | ≥12 % | — |
| Oil hardened and temperedSpecified, limiting ruling section 150 mm; hardness for guidance onlyIS 1570 (Part 4):1988, Table 4, 40Ni6Cr4Mo3 | 890–1040 MPa129–151 ksi | ≥650 MPa≥94 ksi | ≥15 % | 255–311 HB |
| Soft annealed (+A)Maximum hardnessSaarstahl, 34CrNiMo6 datasheet | — | — | — | ≤248 HB |
In practice
Behaviour, heat treatment and uses
Characteristics
- Hardenability is very high. Nickel, chromium and molybdenum together let large sections harden through in oil, which is why the grade is chosen for heavy forgings.
- Toughness is good, including relatively good impact properties at low temperatures, at strengths of 1000 MPa and above.
- Wear resistance is good in the hardened and tempered condition.
- Machinability is rated about 50–57% of AISI 1212 in the annealed condition, depending on the reference. EN24 is normally machined in the supplied hardened and tempered condition.
- Weldability is poor. Welding needs established preheat and post-heat procedures, and the weld zone will not match the base metal unless the part is re-heat-treated.
- Corrosion resistance is that of ordinary low-alloy steel. Parts are oiled, plated or coated when protection is needed.
- The steel is magnetic.
Heat treatment
- Hardening: 830–860 °C, quench in oil (34CrNiMo6 guidance; US practice is about 830 °C, oil quench).
- Tempering: 540–660 °C for the standard quenched and tempered property ranges; the temperature is chosen to suit the target strength.
- Normalizing: 850–880 °C, then air cool.
- Soft annealing: 650–700 °C with slow furnace cooling, giving ≤248 HB.
- Forging: about 1100–850 °C.
主な用途
- Highly stressed shafts, axles and crankshafts
- Gears and heavy-duty transmission parts
- Heavy forgings and large components with big hardened sections
- Automotive, engine and heavy-vehicle parts
- Drill bushings, retaining rings and tooling parts
Alloy and case-hardening steels
Similar grades compared
| グレード | C % | Mn % | Cr % | Ni % | Tensile, first listed condition |
|---|---|---|---|---|---|
| 4340 / EN24 | 0.38–0.43 | 0.60–0.80 | 0.70–0.90 | 1.65–2.00 | 745 MPa |
| 4130 / 25CrMo4 | 0.28–0.33 | 0.40–0.60 | 0.80–1.10 | ≤0.25 | 590–760 MPa |
| 4135 / 34CrMo4 | 0.33–0.38 | 0.70–0.90 | 0.80–1.10 | ≤0.25 | 1000–1200 MPa |
| 4140 / 42CrMo4 | 0.38–0.43 | 0.75–1.00 | 0.80–1.10 | ≤0.25 | 655 MPa |
| 5140 / 41Cr4 | 0.38–0.43 | 0.70–0.90 | 0.70–0.90 | ≤0.25 | 570 MPa |
| 6150 / 51CrV4 | 0.48–0.53 | 0.70–0.90 | 0.80–1.10 | ≤0.40 | 670 MPa |
| 16MnCr5 | 0.13–0.18 | 0.70–0.90 | 0.70–0.90 | ≤0.25 | ≥1000 MPa |
| 20MnCr5 | 0.17–0.22 | 0.70–0.90 | 0.70–0.90 | ≤0.25 | ≥1200 MPa |
| 655M13 / EN36A | 0.08–0.13 | 0.45–0.65 | 1.00–1.40 | 3.00–3.50 | 700–770 MPa |
| 8620 / 20NiCrMo2-2 | 0.18–0.23 | 0.70–0.90 | 0.40–0.60 | 0.40–0.70 | 530 MPa |
Composition from the US standard where one exists, otherwise the first standard listed on each grade's page. Strength conditions differ between grades; open a grade for its full table.
よくあるご質問
Common questions
What is EN24 equivalent to?
EN24 is the old BS 970 name for 817M40. It is usually equated with AISI 4340 in the USA, 34CrNiMo6 (1.6582) in Europe, 40Ni6Cr4Mo3 in India and SNCM439 in Japan. None of these is chemically identical to EN24, so treat them as closest equivalents.
Is EN24 the same as 4340?
No, but they are close and often substituted. EN24 (817M40) has 1.30–1.70% nickel and 1.00–1.40% chromium, while 4340 has 1.65–2.00% nickel and 0.70–0.90% chromium. Both are nickel-chromium-molybdenum steels used hardened and tempered for similar parts.
What is the difference between EN19 and EN24?
EN19 (708M40) is a chromium-molybdenum steel without nickel. EN24 (817M40) adds about 1.5% nickel and more chromium, giving higher hardenability and toughness in large sections. EN24 costs more and is chosen when section size or impact toughness demands it.
What does EN24T mean?
T is the BS 970 heat-treated condition with 850–1000 MPa tensile strength and typically 248–302 HB. Higher letters, such as V at 1000–1150 MPa, denote stronger conditions. The condition that can be reached depends on the ruling section.
Is 34CrNiMo6 the same as 4340?
They are close but not the same. 34CrNiMo6 has lower carbon (0.30–0.38%), less nickel and more chromium than 4340. Both are quenched and tempered nickel-chromium-molybdenum steels for heavily loaded parts.
From the Corona catalog
Need a part made to this specification?
Send the drawing, the material or grade, the finish, the quantity and the delivery country. The team reviews the requirement and the manufacturing route.
お問い合わせを始めるKeep reading
Related references
References
Sources
- Alro Steel, 4340 hot rolled Q&T grade information — AISI 4340 bar composition.
- AZoM, AISI 4340 Alloy Steel (UNS G43400) — Typical annealed properties, machinability rating, US heat-treatment practice, welding note.
- Total Materia, ASTM A322 4340 — Confirms C, Mn and Cr ranges for 4340.
- Smiths Metal Centres, EN24 technical datasheet — 817M40 composition, BS 970 conditions T to Z, related specifications.
- Saarstahl, Werkstoff-Datenblatt 34CrNiMo6 (1.6582) — +QT properties by diameter, heat treatment, cross-references to 817M40, 816M40, SAE 4337 and 4340.
- MARKS GmbH, Werkstoffblatt 1.6582 34CrNiMo6 — EN 10083-3 analysis limits.
- Bureau of Indian Standards, IS 1570 (Part 4):1988 Schedules for wrought steels, alloy steels (Public.Resource.Org copy) — Table 1 composition for 40Ni6Cr4Mo3 and 40Ni6Cr4Mo2; Table 4 hardened and tempered properties.
- Total Materia, IS 40Ni2Cr1Mo28 — Legacy Indian designation under IS 4368:1967.
- USI Steels, JIS G 4053 SNCM439 — Supplier listing of SNCM439 composition; verify against JIS G 4053.
- Wikipedia, 4340 steel — Equivalent-grade list (including SNCM447) and machinability rating.
Values summarize published limits and typical data. The governing standard and the current edition control; check them before specifying.