Materials & grades
17-4PH / 630 / 1.4542 precipitation-hardening stainless steel: S17400, X5CrNiCuNb16-4 and SUS630
17-4PH is a martensitic precipitation-hardening stainless steel with 17 % chromium, 4 % nickel and 4 % copper that ages to over 1300 MPa tensile strength. It is also called Type 630 or UNS S17400, and its equivalents are 1.4542 (X5CrNiCuNb16-4) and SUS630.
Names by standard
What it is called in each region
| Region | System | Designation | मानक | Match |
|---|---|---|---|---|
| USA | AISI/ASTM | 630Type 630 and 17-4PH are the same grade (Atlas). | ASTM A564 (bar, wire, shapes); ASTM A693 (plate, sheet, strip) | Same material |
| Common name | 17-4PHTrade name for Type 630, from the 17 % chromium and 4 % nickel. | — | Same material | |
| UNS | S17400 | — | Same material | |
| EU | EN 10027-1 name | X5CrNiCuNb16-4Silicon, manganese and sulphur limits differ slightly from ASTM A564. | EN 10088-1; EN 10088-2; EN 10088-3 | Equivalent |
| EN 10027-2 number | 1.4542Material number of X5CrNiCuNb16-4. The remelted aerospace variant is 1.4548. | EN 10088-1; EN 10088-2; EN 10088-3 | Equivalent | |
| Japan | JIS G 4303 | SUS630Composition matches ASTM 630. JIS names conditions S, H900, H1025, H1075 and H1150. | JIS G 4303 (bar); JIS G 4304 / G 4305 (plate, sheet) | Equivalent |
On equivalence
- 17-4PH, Type 630, UNS S17400 and AISI 630 are the same steel. 1.4542 and SUS630 are the usual equivalents. EN allows silicon up to 0.70 % and manganese up to 1.50 %, and sets sulphur at 0.015 %. ASTM A564 allows silicon and manganese up to 1.00 % and sulphur 0.030 %.
- No UK designation is listed. BS 970 had no 17-4PH grade, and Atlas and Aircraft Materials show no BS entry. UK buyers specify 1.4542 or ASTM A564 and the aerospace specification.
- No Indian designation appears in IS 1570 (Part 5). Indian buyers order against ASTM A564, EN 10088 or JIS and name the condition.
- Condition names differ. ASTM and JIS use H900, H1025 and H1150, while EN uses +P800, +P930, +P960 and +P1070 for bar and P850, P950 and P1070 for flat products.
- JIS SUS630 H900 yield is 1175 MPa against 1170 MPa in ASTM A564. Check the specification ordered.
- Aerospace specifications (AMS 5643, AMS 5622 for the remelted grade) add requirements beyond the commercial standards.
Chemical composition
Composition limits, mass %
| Element | 630 (S17400)USA · ASTM A564 / A693 | X5CrNiCuNb16-4 (1.4542)EU · EN 10088-1 | SUS630Japan · JIS G 4303 |
|---|---|---|---|
| C | ≤0.07 | ≤0.07 | ≤0.07 |
| Si | ≤1.00 | ≤0.70 | ≤1.00 |
| Mn | ≤1.00 | ≤1.50 | ≤1.00 |
| P | ≤0.040 | ≤0.040 | ≤0.040 |
| S | ≤0.030 | ≤0.015 (≤0.030 bar) | ≤0.030 |
| Cr | 15.0–17.5 | 15.0–17.0 | 15.50–17.50 |
| Ni | 3.0–5.0 | 3.0–5.0 | 3.00–5.00 |
| Mo | — | ≤0.60 | — |
| Cu | 3.0–5.0 | 3.0–5.0 | 3.00–5.00 |
| Nb | — | 5×C–0.45 | 0.15–0.45 |
| Nb+Ta | 0.15–0.45 | — | — |
Mechanical properties
Strength and hardness
| Condition | Tensile strength | Yield strength | Elongation | Hardness |
|---|---|---|---|---|
| Condition A (solution treated)Typical values; hardness is a maximumASTM A564M as quoted by Atlas Steels | 1105 MPa160 ksi | 1000 MPa145 ksi | 15 % | ≤38 HRC (≤363 HB) |
| H900 (aged at 480 °C, 1 h)Specified minimums, bar; hardness is a minimumASTM A564M as quoted by Atlas Steels | ≥1310 MPa≥190 ksi | ≥1170 MPa≥170 ksi | ≥10 % | ≥40 HRC (388 HB) |
| H925 (aged at 495 °C, 4 h)Specified minimums, barASTM A564M as quoted by Atlas Steels | ≥1170 MPa≥170 ksi | ≥1070 MPa≥155 ksi | ≥10 % | ≥38 HRC (375 HB) |
| H1025 (aged at 550 °C, 4 h)Specified minimums, barASTM A564M as quoted by Atlas Steels | ≥1070 MPa≥155 ksi | ≥1000 MPa≥145 ksi | ≥12 % | ≥35 HRC (331 HB) |
| H1075 (aged at 580 °C, 4 h)Specified minimums, barASTM A564M as quoted by Atlas Steels | ≥1000 MPa≥145 ksi | ≥860 MPa≥125 ksi | ≥13 % | ≥32 HRC (311 HB) |
| H1100 (aged at 595 °C, 4 h)Specified minimums, barASTM A564M as quoted by Atlas Steels | ≥965 MPa≥140 ksi | ≥795 MPa≥115 ksi | ≥14 % | ≥31 HRC (302 HB) |
| H1150 (aged at 620 °C, 4 h)Specified minimums, barASTM A564M as quoted by Atlas Steels | ≥930 MPa≥135 ksi | ≥725 MPa≥105 ksi | ≥16 % | ≥28 HRC (277 HB) |
| H900 (SUS630)Specified minimums, bar; reduction of area ≥40 %JIS G 4303 as given by Nose Stainless | ≥1310 MPa≥190 ksi | ≥1175 MPa≥170 ksi | ≥10 % | ≥40 HRC (≥375 HBW) |
| H1150 (SUS630)Specified minimums, bar; reduction of area ≥50 %JIS G 4303 as given by Nose Stainless | ≥930 MPa≥135 ksi | ≥725 MPa≥105 ksi | ≥16 % | ≥28 HRC (≥277 HBW) |
| Aged to P1070 (1.4542)Specified minimums, plate up to 50 mm; elongation A for ≥3 mmEN 10088-2 as tabulated by Euro Inox | 1070–1270 MPa155–184 ksi | ≥1000 MPa≥145 ksi | ≥10 % | — |
| Aged to P950 (1.4542)Specified minimums, plate up to 50 mm; elongation A for ≥3 mmEN 10088-2 as tabulated by Euro Inox | 950–1150 MPa138–167 ksi | ≥800 MPa≥116 ksi | ≥12 % | — |
| Aged to P850 (1.4542)Specified minimums, plate up to 50 mm; elongation A for ≥3 mmEN 10088-2 as tabulated by Euro Inox | 850–1050 MPa123–152 ksi | ≥600 MPa≥87 ksi | ≥14 % | — |
| Solution treated and aged 4 h at 550 °C (X17U4)Typical values, not minimumsAubert & Duval X17U4 data sheet | 1070 MPa155 ksi | 1000 MPa145 ksi | 10 % | Impact 120 J (KV) |
| Solution treated and aged 4 h at 620 °C (X17U4)Typical values, not minimumsAubert & Duval X17U4 data sheet | 950 MPa138 ksi | 750 MPa109 ksi | 16 % | Impact 140 J (KV) |
In practice
Behaviour, heat treatment and uses
Characteristics
- Supplied solution treated, when it is just machinable. One low-temperature aging treatment then hardens it with no significant distortion (Atlas). This suits long shafts that cannot be re-straightened.
- Shrinks slightly on aging, about 0.05 % for H900 and 0.10 % for H1150 (Atlas).
- Condition names follow the aging temperature in °F: H900 is aged at about 480 °C and H1150 at about 620 °C. Higher aging gives lower strength, higher toughness and better stress-corrosion resistance.
- Corrosion resistance approaches 304 (Atlas). It pits and crevice-corrodes in warm chloride water. It has been used for fresh-water boat shafts and, with cathodic protection, in sea water.
- Highly resistant to stress corrosion cracking if aged at 550 °C or above. NACE MR0175 allows 630 only in a double-aged condition (Atlas).
- Do not use the solution-treated condition in service. It has lower stress-corrosion resistance and lower ductility than the aged conditions.
- Martensitic and magnetic. Weldable by standard methods without preheat; post-weld aging restores near-parent properties (Atlas). Machinability is similar to 304. Avoid long exposure at 370–480 °C if toughness matters.
Heat treatment
- Solution treatment (Condition A): about 1040 °C for half an hour, cool in air to below 30 °C. Oil quenching is possible for small non-intricate sections (Atlas). EN sources give 1000–1050 °C and JIS gives 1020–1060 °C.
- H900: age about 480 °C for 1 hour, air cool. JIS gives 470–490 °C.
- H1025: age about 550 °C for 4 hours, air cool. JIS gives 540–560 °C.
- H1150: age about 620 °C for 4 hours, air cool. JIS gives 610–630 °C. Double-aged H1150M and H1150D are specified separately in ASTM A564.
- Aubert & Duval name the two common routes as 4 hours at 550 °C (1070 MPa) and 4 hours at 620 °C (950 MPa). Aging for 1 hour at about 480 °C gives about 1300 MPa but raises stress-corrosion risk.
सामान्य उपयोग
- High-strength pump and boat propeller shafts
- Gears, bolts and valve components
- Plastic moulding dies
- Engine and aerospace components
- Parts needing corrosion resistance with high strength or hardness
Stainless steels
Similar grades compared
| ग्रेड | C % | Mn % | Cr % | Ni % | Tensile, first listed condition |
|---|---|---|---|---|---|
| 17-4PH / 630 | ≤0.07 | ≤1.00 | 15.0–17.5 | 3.0–5.0 | 1105 MPa |
| 201 / 1.4372 | ≤0.15 | 5.50–7.50 | 16.0–18.0 | 3.5–5.5 | ≥515 MPa |
| 301 / 1.4310 | ≤0.15 | ≤2.00 | 16.0–18.0 | 6.0–8.0 | ≥515 MPa |
| 303 / 1.4305 | ≤0.15 | ≤2.0 | 17.0–19.0 | 8.0–10.0 | 650 MPa |
| 304 / 1.4301 | ≤0.08 | ≤2.00 | 18.0–20.0 | 8.0–10.5 | ≥515 MPa |
| 304L / 1.4307 | ≤0.030 | ≤2.00 | 18.0–20.0 | 8.0–12.0 | ≥485 MPa |
| 309 / 309S | ≤0.08 | ≤2.00 | 22.0–24.0 | 12.0–15.0 | ≥515 MPa |
| 310 / 310S | ≤0.08 | ≤2.00 | 24.0–26.0 | 19.0–22.0 | ≥515 MPa |
| 316 / 1.4401 | ≤0.08 | ≤2.00 | 16.0–18.0 | 10.0–14.0 | ≥515 MPa |
| 316L | ≤0.030 | ≤2.00 | 16.0–18.0 | 10.0–14.0 | ≥485 MPa |
Composition from the US standard where one exists, otherwise the first standard listed on each grade's page. Strength conditions differ between grades; open a grade for its full table.
आपके सवालों के जवाब
Common questions
What do H900, H1025 and H1150 mean for 17-4PH?
They name the aging temperature in °F after solution treatment. H900 is aged at about 480 °C and gives the highest strength (at least 1310 MPa, 40 HRC). H1025 is about 550 °C and H1150 about 620 °C, giving lower strength (at least 930 MPa for H1150) but better toughness and stress-corrosion resistance.
Is 17-4PH stainless steel magnetic?
Yes. 17-4PH is martensitic and ferromagnetic in the solution-treated and aged conditions, like 410, 420 and 431.
What is the equivalent of 17-4PH?
1.4542 (X5CrNiCuNb16-4) in Europe and SUS630 in Japan. 630 and S17400 are the same grade as 17-4PH. There is no BS 970 or IS 1570 equivalent.
What is the difference between 17-4PH and 304 or 316?
17-4PH is much stronger, reaching over 1300 MPa after aging, and can be hardened with one low-temperature treatment. Corrosion resistance is about the same as 304 and below 316. 304 and 316 are non-magnetic when annealed and cannot be heat hardened.
Can 17-4PH be welded?
Yes, by standard methods and usually without preheat. Age the weld after welding to restore properties near the parent metal. Design to avoid concentration of weld stresses.
From the Corona catalog
Need a part made to this specification?
Send the drawing, the material or grade, the finish, the quantity and the delivery country. The team reviews the requirement and the manufacturing route.
पूछताछ शुरू करेंKeep reading
Related references
References
Sources
- Atlas Steels, Stainless Steel 630 (17-4PH) Grade Data Sheet (revised 28/04/2021) — ASTM A564M composition and H-condition properties, corrosion, heat treatment, welding.
- Aubert & Duval: X17U4 (X5CrNiCuNb16-4) data sheet — Typical properties for 550 and 620 °C aging, heat treatment and impact values.
- Euro Inox, Stainless Steel: Tables of Technical Properties (2nd edition, 2007) — EN 10088 composition limits and EN 10088-2 flat-product mechanical properties.
- Outokumpu: Steel Grades, Properties and Global Standards — EN, ASTM, UNS, JIS and BS cross-reference; EN and ASTM minimum properties for flat products.
- Nose Stainless: steel types, composition and mechanical properties (JIS G 4303 reference sheet) — JIS G 4303 composition, heat treatment and mechanical properties for bar. Catalog reproducing the JIS values.
- Atlas Steels Technical Handbook of Stainless Steels (revised 12/08/2021) — Grade comparison (BS, EN, JIS), magnetic response and family characteristics. Distributor handbook quoting ASTM values.
- Aircraft Materials: cross-reference of stainless steel specifications — BS and EN numbers (EN56C, EN57, EN60, BS 318S13) against AISI grades. Trade reference.
- MARKS GmbH: Werkstoffblatt 1.4542 X5CrNiCuNb16-4 — EN 10088 aging condition names (+P800, +P930, +P960, +P1070) and heat treatment routes.
Values summarize published limits and typical data. The governing standard and the current edition control; check them before specifying.